Chemical Product |
CAS # |
BTT (minutes) |
Permeation level |
Standard |
Degradation level |
Rating |
1,1,1-Trichloroethane 99% |
71-55-6 |
7 |
0 |
ASTM F739 |
NT |
NA
|
1,1,1,2,2,3,4,5,5,5-Decafluoropentane 97% |
138495-42-8 |
13 |
1 |
ASTM F739 |
NT |
NA
|
1,1,2-Trichlorotrifluoroethane (Freon TF or Freon 113) 99% |
76-13-1 |
20 |
1 |
ASTM F739 |
1 |
-
|
1,2 Dichloroethylene 98% |
156-60-5 |
2 |
0 |
ASTM F739 |
2 |
-
|
1,3 Ethoxy propionate (Ethyl 3-ethoxypropionate) 99% |
763-69-9 |
480 |
6 |
ASTM F739 |
NT |
NA
|
2-Butoxyethanol (Butyl Cellusolve) 99% |
111-76-2 |
53 |
2 |
ASTM F739 |
NT |
NA
|
2-Butoxyethylacetate (Butyl cellosolve acetate) 85% |
112-07-2 |
35 |
2 |
ASTM F739 |
NT |
NA
|
2-Ethoxyethanol (Cellosolve) 99% |
110-80-5 |
27 |
1 |
ASTM F739 |
NT |
NA
|
2-Ethoxyethyl acetate (Cellosolve Acetate) 99% |
111-15-9 |
14 |
1 |
ASTM F739 |
4 |
+
|
2-Methoxyethanol (Methyl Cellosolve) 99% |
109-86-4 |
40 |
2 |
ASTM F739 |
NT |
NA
|
2-Methoxyethanol Acetate (Methyl cellosolve acetate) 98% |
110-49-6 |
27 |
1 |
ASTM F739 |
NT |
NA
|
2-Propanol (Isopropanol) 99% |
67-63-0 |
38 |
2 |
ASTM F739 |
4 |
+
|
4,4 - diamino diphenylsulfone 97% |
80-008-0 |
480 |
6 |
ASTM F739 |
NT |
NA
|
4,4'-Methylenedianiline (MDA) 15% and 15% Methanol mixture |
101-77-9 |
19 |
1 |
ASTM F739 |
NT |
NA
|
4,4'-Methylenedianiline (MDA) 15% in Toluene mixture |
101-77-9 |
15 |
1 |
ASTM F739 |
NT |
NA
|
Acetic acid 10% |
64-19-7 |
NT |
NT |
|
4 |
NA
|
Acetic acid 50% |
64-19-7 |
NT |
NT |
|
4 |
NA
|
Acetic acid 99% |
64-19-7 |
32 |
2 |
ASTM F739 |
4 |
+
|
Acetone 99% |
67-64-1 |
6 |
0 |
ASTM F739 |
4 |
=
|
Aluminum Etch mixture |
NA |
960 |
5 |
ASTM F739 |
4 |
++
|
Aluminum Oxide mixture |
NA |
55 |
2 |
ASTM F739 |
NT |
NA
|
Ammonium Fluoride 40% |
12125-01-8 |
480 |
6 |
ASTM F739 |
NT |
NA
|
Ammonium Fluoride 79% |
12125-01-8 |
480 |
6 |
ASTM F739 |
NT |
NA
|
Ammonium hydroxide solution 29% |
1336-21-6 |
36 |
2 |
ASTM F739 |
4 |
+
|
Baker PRS-1000 mixture |
NA |
20 |
1 |
ASTM F739 |
NT |
NA
|
Baker PRS-2000 mixture |
NA |
130 |
4 |
ASTM F739 |
NT |
NA
|
Baker PRS-3000 mixture |
NA |
480 |
6 |
ASTM F739 |
NT |
NA
|
Benzene 99% |
71-43-2 |
4 |
0 |
ASTM F739 |
1 |
-
|
Buffered Oxide Etch mixture |
NA |
480 |
6 |
ASTM F739 |
4 |
++
|
Butyl Acetate 99% |
123-86-4 |
7 |
0 |
ASTM F739 |
4 |
=
|
Chromic Acid 50% |
7738-94-5 |
60 |
2 |
ASTM F739 |
NT |
NA
|
Cyclohexanone 99% |
108-94-1 |
23 |
1 |
ASTM F739 |
1 |
-
|
Cyclopentanone 99% |
120-92-3 |
11 |
1 |
ASTM F739 |
NT |
NA
|
Dichloromethane (Methylene Chloride) 99% |
75-09-2 |
4 |
0 |
ASTM F739 |
NT |
NA
|
Dichromate cleaning solution mixture |
NA |
480 |
6 |
ASTM F739 |
4 |
++
|
Diethylamine 98% |
109-89-7 |
4 |
0 |
ASTM F739 |
NT |
NA
|
Diglycidal ether of bisphenol 100% |
25068-38-6 |
480 |
6 |
ASTM F739 |
NT |
NA
|
Dimethylamine 35% |
124-40-3 |
53 |
2 |
ASTM F739 |
NT |
NA
|
Dimethylformamide 99% |
68-12-2 |
8 |
0 |
ASTM F739 |
NT |
NA
|
Dimethylsulfoxide 99% |
67-68-5 |
181 |
4 |
ASTM F739 |
4 |
++
|
Epichlorohydrin 99% |
106-89-8 |
4 |
0 |
ASTM F739 |
NT |
NA
|
Ethanol 95% |
64-17-5 |
21 |
1 |
ASTM F739 |
NT |
NA
|
Ethyl lactate 95% |
97-64-3 |
29 |
1 |
ASTM F739 |
NT |
NA
|
Ethylene glycol 99% |
107-21-1 |
480 |
6 |
ASTM F739 |
4 |
++
|
Hexamethyldisilazane (HMDS) 98% |
999-97-3 |
18 |
1 |
ASTM F739 |
1 |
-
|
Hydrochloric acid 10% |
7647-01-0 |
480 |
6 |
EN 374-3:2003 |
4 |
++
|
Hydrochloric acid 35% |
7647-01-0 |
NT |
NT |
|
4 |
NA
|
Hydrochloric acid 37% |
7647-01-0 |
454 |
5 |
ASTM F739 |
4 |
++
|
Hydrofluoric Acid 10% |
7664-39-3 |
NT |
NT |
|
4 |
NA
|
Hydrofluoric Acid 49% |
7664-39-3 |
390 |
5 |
ASTM F739 |
NT |
NA
|
Hydrogen peroxide 30% |
7722-84-1 |
960 |
5 |
ASTM F739 |
4 |
++
|
Hydrotreated Light Naphthenic Distillate mixture |
64742-53-6 |
161 |
4 |
ASTM F739 |
2 |
+
|
Kerosene mixture |
8008-20-6 |
26 |
1 |
ASTM F739 |
1 |
-
|
KOH Etch mixture |
NA |
278 |
5 |
ASTM F739 |
4 |
++
|
KTI Pad Etch mixture |
NA |
480 |
6 |
ASTM F739 |
NT |
NA
|
KTI Silicon Etch mixture |
NA |
480 |
6 |
ASTM F739 |
NT |
NA
|
Methanesulfonic Acid 99% |
75-75-2 |
NT |
NT |
|
4 |
NA
|
Methanol 85% |
67-56-1 |
19 |
1 |
ASTM F739 |
4 |
+
|
Methanol 99% |
67-56-1 |
NT |
NT |
|
4 |
NA
|
Methyl Amyl Ketone 98% |
110-43-0 |
8 |
0 |
ASTM F739 |
1 |
-
|
Methyl Ethyl Ketone (2-Butanone) 99% |
78-93-3 |
4 |
0 |
ASTM F739 |
3 |
=
|
Methyl-3-methoxypropionate 100% |
3852-09-3 |
11 |
1 |
ASTM F739 |
3 |
=
|
n-hexane 95% |
110-54-3 |
3 |
0 |
ASTM F739 |
1 |
-
|
N-methyl-2-Pyrrolidone 99% |
872-50-4 |
50 |
2 |
ASTM F739 |
4 |
+
|
N-N dimethyl acetamide 99% |
127-19-5 |
47 |
2 |
ASTM F739 |
NT |
NA
|
Naphtha VM&P mixture |
8032-32-4 |
2 |
0 |
ASTM F739 |
1 |
-
|
Nitric acid 10% |
7697-37-2 |
840 |
5 |
ASTM F739 |
4 |
++
|
Nitric acid 20% |
7697-37-2 |
480 |
6 |
ASTM F739 |
4 |
++
|
Nitric acid 40% |
7697-37-2 |
480 |
6 |
ASTM F739 |
4 |
++
|
Nitric acid 50% |
7697-37-2 |
NT |
NT |
|
4 |
NA
|
Nitric acid 68% |
7697-37-2 |
299 |
5 |
EN 374-3:2003 |
4 |
++
|
Nitric acid 70% |
7697-37-2 |
307 |
5 |
ASTM F739 |
4 |
++
|
Nitric acid 90% |
7697-37-2 |
7 |
0 |
ASTM F739 |
NT |
NA
|
Nitride Etch mixture |
NA |
NT |
NT |
|
4 |
NA
|
Nitrohydrochloric acid (Aqua Regia) mixture |
8007-56-5 |
480 |
6 |
ASTM F739 |
NT |
NA
|
Phenol 85% |
108-95-2 |
102 |
3 |
ASTM F739 |
4 |
++
|
Phosphoric acid 75% |
7664-38-2 |
480 |
6 |
ASTM F739 |
4 |
++
|
Phosphoric acid 85% |
7664-38-2 |
480 |
6 |
ASTM F739 |
4 |
++
|
Phosphorus Oxychloride 99% |
10025-87-3 |
15 |
1 |
ASTM F739 |
NT |
NA
|
Piranha Etch mixture |
NA |
243 |
5 |
ASTM F739 |
1 |
-
|
Polyethylene glycol octylphenyl ether 100% |
9002-93-1 |
480 |
6 |
ASTM F739 |
NT |
NA
|
Potassium Hydroxide 50% |
1310-58-3 |
480 |
6 |
ASTM F739 |
4 |
++
|
Potassium Hydroxide Etch mixture |
NA |
24 |
1 |
ASTM F739 |
NT |
NA
|
Propylene Glycol 99% |
57-55-6 |
480 |
6 |
ASTM F739 |
4 |
++
|
Propylene Glycol Methyl Ethyl Acetate (PGMEA) 99% |
108-65-6 |
47 |
2 |
ASTM F739 |
3 |
+
|
Propylene Glycol Monomethyl Ether 99% |
107-98-2 |
26 |
1 |
ASTM F739 |
4 |
+
|
Silicon Tetrachloride 100% |
10026-04-7 |
15 |
1 |
ASTM F739 |
NT |
NA
|
Slope Etch mixture |
NA |
260 |
5 |
ASTM F739 |
4 |
++
|
Sodium hydroxide 20% |
1310-73-2 |
780 |
5 |
ASTM F739 |
4 |
++
|
Sodium hydroxide 40% |
1310-73-2 |
780 |
5 |
ASTM F739 |
4 |
++
|
Sodium hydroxide 50% |
1310-73-2 |
780 |
5 |
ASTM F739 |
4 |
++
|
Sulfuric acid 10% |
7664-93-9 |
900 |
5 |
ASTM F739 |
4 |
++
|
Sulfuric acid 96% |
7664-93-9 |
102 |
3 |
ASTM F739 |
1 |
-
|
Tetrachloroethylene (Perchloroethylene) 99% |
127-18-4 |
4 |
0 |
ASTM F739 |
1 |
-
|
Tetraethyl Orthosilicate 100% |
78-10-4 |
25 |
1 |
ASTM F739 |
1 |
-
|
Tetramethyl Ammonium Hydroxide 25% |
75-59-2 |
480 |
6 |
ASTM F739 |
4 |
++
|
Thionylchloride 99% |
7719-09-7 |
15 |
1 |
ASTM F739 |
NT |
NA
|
Toluene 49% Methyl Isobutyl Ketone 34.5% Methyl Ethyl Ketone 16.5% mixture |
NA |
1 |
0 |
EN 374-3:2003 |
NT |
NA
|
Toluene Diisocyanate (TDI) 80% |
584-84-9 |
27 |
1 |
ASTM F739 |
NT |
NA
|
Trichloroethylene 99% |
79-01-6 |
NT |
NT |
|
1 |
NA
|
Trimethylphosphite 97% |
121-45-9 |
10 |
0 |
ASTM F739 |
NT |
NA
|
Unleaded gasoline mixture |
8006-61-9 |
4 |
0 |
ASTM F739 |
1 |
-
|
Xylene 99% |
1330-20-7 |
4 |
0 |
ASTM F739 |
1 |
-
|